Title: | Studies on the Solid Oxide Cell Perovskite Electrode Materials for Soot Oxidation Activity |
Authors: | Shenoy, C.S. Patil, S.S. Govardhan, P. Shourya, A. Dasari, Hari Prasad Saidutta, M.B. Dasari, H. |
Issue Date: | 2019 |
Citation: | Emission Control Science and Technology, 2019, Vol.5, 4, pp.342-352 |
Abstract: | Solid oxide cell (SOC) perovskite electrode materials (BSCF (Ba0.5Sr0.5Co0.8Fe0.2O3-?), LSCF (La0.6Sr0.4Co0.2Fe0.8O3-?) and LSCM (La0.75Sr0.25Cr0.5Mn0.5O3-?)) were synthesised using microwave-assisted reverse-strike co-precipitation method and tested for soot oxidation activity. The calcined perovskite materials were characterized using FT-IR, XRD, SEM and BSE, BET and BJH and XPS analysis. The mean activation energy for soot oxidation was calculated from Ozawa plots at various heating rates (5, 10, 15 and 20 K/min) at different levels of soot conversions (T10 to T90) for BSCF, LSCM and LSCF perovskite materials and was around 133 11.5, 138 9.9 and 152 7.2 kJ/mol, respectively. Irrespective of the heating rates, BSCF material showed the lowest T50 temperature than compared to other samples, and it is correlated to the presence of Fe3O4 as a secondary phase. 2019, Springer Nature Switzerland AG. |
URI: | https://idr.nitk.ac.in/jspui/handle/123456789/13113 |
Appears in Collections: | 1. Journal Articles |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
10 Studies on the Solid Oxide.pdf | 2.22 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.