Structural, electrical and optical properties of stoichiometric In2Te3 thin films

Abstract

In2Te3 thin films were grown by thermal evaporation technique. The annealing of films played a major role to obtain stoichiometry, regardless of substrate temperature. Annealing at 300 ?C resulted in well oriented, mono-phased and nearly stoichiometric In2Te3 thin films. The variation in grain size of In2Te3 films associated with the substrate temperatures provides a significant control over the resistivity of the films, and the resistivity decreased with an increase in the grain size. The activation energy and optical band gap of stoichiometric In2Te3 films were found to be 0.01 0.005 eV and 0.99 0.02 eV, respectively. The absorption co-efficient of these films was found to be of the order of 105 cm?1. 2016 Elsevier Ltd and Techna Group S.r.l.