dc.identifier.citationFatigue & Fracture of Engineering Materials & Structures, 1995, Vol.18, 6, pp.693-697en_US
dc.identifier.urihttp://idr.nitk.ac.in/jspui/handle/123456789/10817-
dc.description.abstractAbstract Studies have been conducted on the effect of overstressing in rotary bending fatigue on the fatigue properties of an annealed and austempered ductile iron containing 1.5 Ni 0.3 Mo. For various R ratios S N curves were determined and the fatigue limit estimated. It was found that the fatigue limit was a function of the level of overstressing and cycle ratio. In the case of austempered samples a beneficial effect of overstressing was observed at a certain level of overstressing. This was related to the work hardening behaviour of the austenite phase. In annealed samples, a reduction in the fatigue limit was observed at all levels of overstressing. Copyright 1995, Wiley Blackwell. All rights reserveden_US
dc.titleEFFECT OF OVERSTRESSING ON FATIGUE BEHAVIOUR OF AUSTEMPERED DUCTILE IRONen_US
dc.typeArticleen_US
Appears in Collections:1. Journal Articles

Files in This Item:
There are no files associated with this item.


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.